紫外熔融石英高精度窗口
特性
l 紫外熔融石英基底
l 可选择未镀膜或者镀有下列四种增透镀膜的中一种
n 290-370纳米(-紫外膜)
n 350-700纳米(-A膜)
n 650-1050纳米(-B膜)
n 1050-1620纳米(-C镀膜)
l 波长范围:185纳米-2.1微米(未镀膜)
(1)Ø1/2英寸(12.7毫米)紫外熔融石英宽带窗口
Item#
|
Diameter
(mm)
|
Thickness
(mm)
|
AR Coating
(nm)
|
Damage Threshold
(10 ns Pulse)
|
WG40530
|
12.7
|
3.0
|
Uncoated
|
32.0 J/cm2
|
WG40530-A
|
12.7
|
3.0
|
350-650
|
1.0 J/cm2
|
WG40530-B
|
12.7
|
3.0
|
650-1050
|
1.0 J/cm2
|
WG40530-C
|
12.7
|
3.0
|
1050-1620
|
0.9 J/cm2
|
(2)Ø1英寸(25.4毫米)紫外熔融石英宽带窗口
Item#
|
Diameter
(mm)
|
Thickness
(mm)
|
AR Coating
(nm)
|
Damage Threshold
10 ns Pulse
|
WG41050
|
25.4
|
5.0
|
Uncoated
|
32.0 J/cm2
|
WG41050-A
|
25.4
|
5.0
|
350-650
|
1.0 J/cm2
|
WG41050-B
|
25.4
|
5.0
|
650-1050
|
1.0 J/cm2
|
WG41050-C
|
25.4
|
5.0
|
1050-1620
|
0.9 J/cm2
|
(3)Ø2英寸(50.8毫米)紫外熔融石英宽带窗口
Item #
|
Diameter
|
Thickness
|
AR Coating
|
Damage Threshold
|
WG42012
|
2"
|
12.0 mm
|
Uncoated
|
-
|
WG42012-UV
|
2"
|
12.0 mm
|
290 - 370 nm
|
5.0 J/cm2 at 355 nm, 10 ns, 10 Hz, Ø0.350 mm
|
WG42012-A
|
2"
|
12.0 mm
|
350 - 700 nm
|
7.5 J/cm2 at 532 nm, 10 ns, 10 Hz, Ø0.491 mm
|
WG42012-B
|
2"
|
12.0 mm
|
650 - 1050 nm
|
7.5 J/cm2 at 810 nm, 10 ns, 10 Hz, Ø0.133 mm
|
WG42012-C
|
2"
|
12.0 mm
|
1050 - 1620 nm
|
7.5 J/cm2 at 1542 nm, 10 ns, 10 Hz, Ø0.189 mm
|
|